A model of damaged medium for evaluating the durability of structures subjected to combined low- and high-cycle fatigue loading
DOI:
https://doi.org/10.7242/1999-6691/2012.5.1.7Keywords:
modeling, stress-strain state, plasticity, damage, failure, low-and high-cycle fatigue, durability, resourceAbstract
In order to evaluate the strength and lifetime of critical engineering structures, we have developed a mathematical model of damaged medium consisting of elastoplastic constitutive equations, kinetic equations of damage accumulation, and a strength criterion of damaged material. A version of the evolution equation describing accumulation of damages caused by a combination of low-cycle fatigue (LCF) and high-cycle fatigue (HSF) mechanisms is proposed. It is shown that under regular cyclic loading, when the amplitude of deformation in a cycle decreases, the transition from low cycle fatigue to high cycle fatigue proceeds gradually and depends on the physical interaction of these mechanisms in the transition zone. A method for determining the parameters of the evolution equation of fatigue damage accumulation is presented. Comparison of the calculated and experimental data shows that the developed model of damage medium adequately describes the durability of structures subjected to combined low- and high-cycle fatigue loading.
Downloads
References
Mahutov N.A., Gadenin M.M. Issledovania nelinejnyh effektov deformirovania i kriteriev razrusenia // Zavodskaa laboratoria. Diagnostika materialov. - 2005. - T. 71, No 8. - S. 57-67.
Kolmogorov V.L., Burdukovskii B.G., Kamantsev I.S. Prediction of damage under multicycle loading // Inorganic Materials. - 2010. - V. 46, N. 14. - P. 1567-1569. DOI
Oakley S.Y., Nowell D. Prediction of the combined high- and low-cycle fatigue performance of gas turbine blades after foreign object damage // Int. J. Fatigue. - V. 29, N. 1. - P. 69-80. DOI
Hou N.X., Wen Z.X., Yu Q.M., Yue Z.F. Application of a combined high and low cycle fatigue life model on life prediction of SC blade // Int. J. Fatigue. - V. 31, N. 4. - P. 616-619. DOI
Schweizer C., Seifert T., Nieweg B., von Hartrott P., Riedel H. Mechanisms and modelling of fatigue crack growth under combined low and high cycle fatigue loading // Int. J. Fatigue. - 2011. - V. 33, N. 2. - P. 194-202. DOI
Kollinz Dz. Povrezdenie materialov v konstrukciah. Analiz. Predskazanie. Predotvrasenie. - M.: Mir, 1984. - 530 s.
Trosenko V.T., Fomicev L.A. Energeticeskij kriterij ustalostnogo razrusenia // Problemy procnosti. - 1993. - No 1. - S. 3-10.
Mitenkov F.M., Kajdalov V.B., Korotkih U.G. Metody obosnovania resursa adernyh energeticeskih ustanovok. - M.: Masinostroenie, 2007. - 448 s.
Volkov I.A., Korotkih U.G. Uravnenia sostoania vazkouprugoplasticeskih sred s povrezdeniami. - M.: Fizmatlit, 2008. - 424 s.
Volkov I.A., Korotkih U.G., Tarasov I.S. Cislennoe modelirovanie nakoplenia ustalostnyh povrezdenij pri sloznom plasticeskom deformirovanii // Vycisl. meh. splos. sred. - 2009. - T. 2, No 1. - S. 5-18.
Bol’suhin M.A., Zverev D.L., Kajdalov V.B., Korotkih U.G. Ocenka dolgovecnosti konstrukcionnyh materialov pri sovmestnyh processah malociklovoj i mnogociklovoj ustalosti // Problemy procnosti i plasticnosti: Mezvuz. sb. / NNGU. - 2010. - No 72. - S. 28-35.
Rukovodstvo po rascetam na procnost’ elementov oborudovania i izdelij reaktornyh ustanovok s vodnym teplonositelem plavucih atomnyh stancij (RP-OIRU-PAS-04). - Moskva: GUP ICP MAE, 2004. - 226 s.
Downloads
Published
Issue
Section
License
Copyright (c) 2012 Computational Continuum Mechanics
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.