Mathematical modeling of failure process of AlMg2.5 alloy during highand very high cycle fatigue
DOI:
https://doi.org/10.7242/1999-6691/2018.11.3.24Keywords:
numerical simulation, very high cycle fatigue, duality of the Weller curve, cyclic loading, fatigue failure, endurance limitAbstract
Forecasting the limit of endurance in the high- and very high cycle loading range (102-1010) is an actual problem of aircraft engine construction and high-speed rail transport. It involves the development of models and their experimental verification, taking into account the stages of development of damage and the development of fatigue cracks in a damaged medium. The proposed model of the damage evolution, taking into account the kinetics of defects and effects of microplasticity, was used to study the process of fatigue failure of a structural alloy AlMg2.5. The model parameters were identified and verified using experimental data on static, dynamic and fatigue loading, as well as tests at various temperatures. The Weller curve is numerically constructed. It agrees well with experiment in the range of high cycle fatigue. The duality effect of the S-N diagram is described. A computational experiment on the effect of dynamic loading on fatigue strength showed a weak dependence of the fatigue limit on preliminary dynamic strain. It is confirmed by experimental data. Comparison of various mathematical packages and numerical methods for solving the constructed system of differential equations carried out. The optimality of the Adams method and its modifications for numerical integration of the problem under consideration is shown. Wolfram Mathematica is the preferred software package for numerical solution. The problem of convergence of the numerical solution has been investigated.
Downloads
References
Coffin L.F. A study of the effect of cyclic thermal stresses on a ductile metal. Trans ASME, 1954, no. 76, pp. 931-950.
Bathias C. There is no infinite fatigue life in metallic materials. Fract. Eng. Mater. Struct., 1999, vol. 22, no. 22, pp. 559-65. DOI
Murakami Y., Nomoto T., Ueda T. Factors influencing the mechanism of superlong fatigue failure in steels. Fract. Eng. Mater. Struct., 1999, vol. 22, no. 22, pp. 581–90. DOI
Terent’yev V.F. Ustalostnaya prochnost’ metallov i splavov [Fatigue strength of metals and alloys]. : Intermet Inzhiniring, 2002. 288 p.
Botvina L.R. Gigatsiklovaya ustalost’ – novaya problema fiziki i mekhaniki razrusheniya [Very high cycle fatigue is a new problem in fracture mechanics and physics]. Zavodskaya laboratoriya. Diagnostika materialov – Industrial Laboratory. Diagnostics of Materials, 2004, vol. 70, no. 4, pp. 41-51.
Mughrabi H. Specific features and mechanisms of fatigue in the ultrahigh-cycle regime. J. Fatig., 2006, vol. 28, no. 11, pp. 1501-1508. DOI
Pang H.T., Reed P.A.S. Microstructure effects on high temperature fatigue crack initiation and short crack growth in turbine nickel-base superalloy Udimet720Li. Sci. Eng., 2007, vol. 448, no. 1-2. P. 67-69. DOI
Froustey C., Lataillade J.L. Influence of the microstructure of aluminium alloys on their residual impact properties after a fatigue loading program. Sci. Eng., 2009, vol. 500, no. 1-2, pp. 155-163. DOI
Palin-Luc T., Perez-Mora R., Bathias C., Dominguez G., Paris P.C., Arana J.L. Fatigue crack initiation and growth on a steel in the very high cycle regime with sea water corrosion. Fract. Mech., 2010, vol. 77, no. 11, pp. 1953-1962. DOI
Oborin V., Bannikov M., Naimark O., Palin-Luc T. Scaling invariance of fatigue crack growth in gigacycle loading regime. Phys. Lett., 2010, vol. 36, no. 11, pp. 1061-1063. DOI
Shanyavskiy A.A. Modelirovaniye ustalostnykh razrusheniy metallov. Sinergetika v aviatsii [Modeling of fatigue fractures of metals. Synergetics in aviation]. Ufa: Monografiya, 2007. 500 p.
Huang Z., Wagner D., Wang Q.Y., Bathias C. Effect of carburizing treatment on the “fish eye” crack growth for a low lloyed chromium steel in very high cycle fatigue. Mater. Sci. Eng., 2013, vol. 559, pp. 790-797. DOI
Nguyen H.Q., Gallimard L., Bathias C. Numerical simulation of fish-eye fatigue crack growth in very high cycle fatigue. Frac. Mech., 2015, vol. 135, pp. 81-93. DOI
Naimark O.B., Plekhov O.A., Betekhtin V.I., Kadomtsev A.G., Narykova M.V. Kinetics of defect accumulation and duality of the weller curve in gigacycle fatigue of metals. Phys., 2014, vol. 59, no. 3, pp. 398-401. DOI
Volkov I.A., Korotkih Yu.G., Panov V.A., Shishulin D.N. Modeling of fatigue damage accumulation in structural steels under low-cycle block loading. mekh. splosh. sred – Computational Continuum Mechanics, 2014, vol. 7, no. 1, pp. 15-22. DOI
Volkov I.A., Igumnov L.A., Tarasov I.S. Evaluating fatigue life of materials and structures under low-cycle loading. mekh. splosh. sred – Computational Continuum Mechanics, 2017, vol. 10, no. 1, pp. 17-30. DOI
Guchinskij R.V., Petinov S.V. Numerical modeling of the semi-elliptical fatigue crack growth using damage accumulation approach. mekh. splosh. sred – Computational Continuum Mechanics, 2015, vol. 8, no. 4, pp. 367-385. DOI
Bilalov D.A., Sokovikov M.A., Chudinov V.V., Oborin V.A., Bayandin Yu.V., Terekhina A.I., Naimark O.B. Study of plastic shear localization in aluminum alloys under dynamic loading. mekh. splosh. sred – Computational Continuum Mechanics, 2015, vol. 8, no. 3, pp. 319-328. DOI
Bilalov D.A., Sokovikov M.A., Chudinov V.V., Oborin V.A., Bayandin Yu.V., Terekhina A.I., Naimark O.B. Numerical modeling and experimental study of plastic strain localization at dynamic loading of samples under conditions close to pure shear. mekh. splosh. sred – Computational Continuum Mechanics, 2017, vol. 10, no. 1, pp. 103-112. DOI
Annin B.D., KorobeynikovN. Dopustimyye formy uprugikh zakonov deformirovaniya v opredelyayushchikh sootnosheniyakh uprugo-plastichnosti [Admissible forms of elastic laws of deformation in the constitutive relations of elastoplasticity]. Sibirskiy zhurnal industrial’noy matematiki – Journal of Applied and Industrial Mathematics, 1998, vol. 1, no. 1, pp. 21-34.
Novokshanov R.S., Rogovoy A.A. O postroyenii evolyutsionnykh opredelyayushchikh uravneniy [On the construction of evolutionary defining equations]. Vestnik PNIPU. Mekhanika – Bulletin of the PNRPU. Mechanics, 2001, no. 9, pp. 103‑109.
Godunov S.K., Demchuk A.F., Kozin N.S., Mali V.I. Interpolation formulas for maxwell viscosity of certain metals as a function of shear-strain intensity and temperature. Appl. Mech. Tech. Phys., 1974, vol. 15, no. 4, pp. 526-529. DOI
Bankina O.S., Dzyuba A.S., Khvatan A.M. Metod postroyeniya diagramm deformirovaniya σ-ε po spravochnym mekhanicheskim kharakteristikam materiala [The method of constructing the deformation diagrams σ-ε by the reference mechanical characteristics of the material]. Trudy TsAGI – TsAGI Science Journal, 2000, no. 2639, pp. 36-38.
Frolov K.V. (ed.) Entsiklopediya [Mechanical Engineering. Encyclopedia]. M.: Mashinostroyeniye, 2001. Vol. II-3: Tsvetnyye metally i splavy. Kompozitsionnyye metallicheskiye materialy [Non-ferrous metals and alloys. Composite metal materials]. 880 p.
Makhutov N.A. Deformatsionnyye kriterii razrusheniya i raschet elementov konstruktsiy na prochnost’ [The deformation fracture criteria and strength calculation of the structural elements]. M.: Mashinostroyeniye, 1981. 272 p.
Downloads
Published
Issue
Section
License
Copyright (c) 2018 Computational Continuum Mechanics
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.